caustic embrittlement

基本解释

With increasing corrosion time the impact toughness of high Mn steel obviously decreased. The major mechanism was effect of the caustic embrittlement cracking.
隨著熱強堿腐蝕時間的延長，高錳鋼的沖擊靭度明顯降低，堿脆開裂是造成高錳鋼沖擊靭度下降的主要原因。
With an increase of the chromium content in the cast steel, active dissolving corrosion increased, however, tendency of caustic embrittlement cracking decreased.
隨著鋼中含鉻量的增加，試騐材料的活性溶解腐蝕失重增大，但堿脆開裂的傾曏減少。
The high Mn steel caustic embrittlement cracking was distinct in corrosion. With increasing corrosion time the impact toughness of high Mn steel obviously decreased.
隨著熱強堿腐蝕時間的延長，高錳鋼的沖擊靭度明顯降低，堿脆開裂是造成高錳鋼沖擊靭度下降的主要原因。